Using Plantain Rachis Fibers and Mopa-Mopa Resin to Develop a Fully Biobased Composite Material.

A completely biobased composite material was developed using a matrix of natural resin extracted from the Elaegia pastoensis Mora plant, commonly known as Mopa-Mopa or "Barniz de Pasto", reinforced with fibers extracted from plantain rachis agricultural residues. A solvent process, involving grinding, distillation, filtration, and drying stages, was implemented to extract the resin from the plant bud. To obtain the resin from the plant bud, the vegetable material was ground and then dissolved in a water-alcohol blend, followed by distillation, filtration, and grinding until the powdered resin was ready for use in the preparation of the biocomposite. Likewise, using mechanical techniques, the plantain rachis fibers were extracted and worked in their native condition and with a previous alkalinization surface treatment. Finally, the biocomposite material was developed with and without incorporating stearic acid, which was included to reduce the material's moisture absorption. Ultimately stearic acid was used as an additive to reduce biocomposite moisture absorption. The tensile mechanical results showed that the Mopa-Mopa resin reached a maximum strength of 20 MPa, which decreased with the incorporation of the additive to 12 MPa, indicating its plasticization effect. Likewise, slight decreases in moisture absorption were also evidenced with the incorporation of stearic acid. With the inclusion of rachis plantain fibers in their native state, a reduction in the tensile mechanical properties was found, proportional to the amount added. On the other hand, with the alkalinization treatment of the fibers, the behavior was the opposite, evidencing increases in tensile strength, indicating that the fiber modification improved the interfacial adhesion with the Mopa-Mopa matrix. On the other hand, the evaluation of the moisture absorption of the biocomposite material evidenced, as expected, that the absorption level was favored by the relative humidity used in the conditioning (47, 77, and 97%), which also had an impact on the decrease of the mechanical tensile properties, being this was slightly counteracted by the inclusion of stearic acid in the formulation of the material.

Use of Organic Acids in Bamboo Fiber-Reinforced Polypropylene Composites: Mechanical Properties and Interfacial Morphology.

In obtaining wood polymer composites (WPCs), a weak interfacial bonding can cause problems during the processing and affect the mechanical properties of the resulting composites. A coupling agent (CA) is commonly used to solving this limitation. To improve the interfacial bonding between bamboo fiber (BF) and a polypropylene matrix, the effect of three organic acids on the mechanical properties and interfacial morphology were investigated. The BF/PP composites were prepared in five families: the first without CA, the second using a maleic anhydride-grafted polypropylene coupling agent, and the third, fourth, and fifth families with the addition of organic acids (OA) tricarboxylic acid (TRIA), hexadecanoic acid (HEXA), and dodecanoic acid (DODA), respectively. The use of OA in BF/PP improved the interfacial adhesion with the PP matrix, and it results in better mechanical performance than composites without CA. Composites coupled with MAPP, TRIA, DODA, and HEXA showed an increase in Young's modulus of about 26%, 23%, 15%, and 16% respectively compared to the composite without CA incorporation. In tensile strength, the increase in composites with CA was about 190%, while in the flexural modulus, the coupled composites showed higher values, and the increase was more in composites with TRIA: about 46%. The improvement caused by tricarboxylic acid was similar to that promoted by the addition of maleic anhydride-grafted polypropylene (MAPP).

Influence of Coupling Agent in Mechanical, Physical and Thermal Properties of Polypropylene/Bamboo Fiber Composites: Under Natural Outdoor Aging.

Researches on thermoplastic composites using natural fiber as reinforcement are increasing, but studies of durability over time are scarce. In this sense the objective of this study is to evaluate changes in the properties of polypropylene/bamboo fiber (PP/BF) composite and the influence of the use of coupling agent (CA) in these composites after natural ageing. The PP/BF (70/30 wt) composites and 3% wt CA (citric acid from natural origin and maleic anhydride grafted polypropylene from petrochemical origin) were prepared by using an internal mixer chamber and then injection-molded. The samples were exposed to natural weathering for a total period of 12 months and characterized before and after exposure. All exposed composites experienced a decrease in their properties, however, the use of CA promoted more stability; in mechanical properties, the composites with CA showed lower loss about 23% in Young's modulus, 18% in tensile stress at break, and 6% in impact strength. This behavior was similar in thermal and physical properties, the result for the CA of natural origin being similar to that of synthetic origin. These results indicate that the use of a CA may promote higher interaction between the fiber and the polymer. In addition, the CAs of organic origin and synthetic origin exhibited similar responses to natural ageing.